13549213581肖生

玻璃纤维增强材料33%,耐水解性, 高强度,金属取代, 良好的流动性, 齿轮, 动力/其它工具,汽车的发动机罩下的零件, 外壳

 

Vydyne® R533H NT

聚酰胺66

Ascend Performance Materials Operations LLC

Technical Data

 

产品说明

 

Vydyne R533H NT is 33% glass-fiber reinforced, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is lubricated for improved machine feed and flow.

 

Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.

 

Vydyne R533H NT resin is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R533H NT resin has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.

 

Typical Applications/End Uses:

Vydyne R533H NT resin has been used for many under-the-hood automotive applications, motor housings for power tools and garden appliances. This resin has also been used in miscellaneous brackets, gears and clips that require high rigidity and strength.

 

总体

 

材料状态 • 已商用：当前有效

资料 1 •  Technical Datasheet

UL 黄卡 2 •  E70062-249086

搜索 UL 黄卡 •  Ascend Performance Materials Operations LLC

•  Vydyne®

供货地区 • 北美洲 • 欧洲 • 亚太地区

填料/增强材料 • 玻璃纤维增强材料, 33% 填料按重量

添加剂 • 热稳定剂 • 润滑剂

特性 • 刚性，高 • 流动性高 • 润滑

• 高强度 • 热稳定性 • 脱模性能良好

用途 • 齿轮 • 汽车的发动机罩下的零件

• 动力/其它工具 • 外壳

机构评级 • ASTM D 4066 PA0121G35 • ASTM D 6779 PA0121G35

UL文件号 • E70062

外观 • 自然色

形式 • 粒子

加工方法 • 注射成型

物理性能 干燥 调节后的 单位制 测试方法

密度 1.40 -- g/cm³ ISO 1183

收缩率 ISO 294-4

垂直流动方向 : 23°C, 2.00 mm 0.90 -- %

流动方向 : 23°C, 2.00 mm 0.40 -- %

吸水率 ISO 62

23°C, 24 hr 0.80 -- %

平衡, 23°C, 50% RH 1.7 -- %

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 10600 7900 MPa ISO 527-2

拉伸应力 (断裂, 23°C) 205 145 MPa ISO 527-2

拉伸应变 (断裂, 23°C) 3.0 5.0 % ISO 527-2

弯曲模量 (23°C) 10200 6500 MPa ISO 178

弯曲应力 (23°C) 290 200 MPa ISO 178

泊松比 0.40 -- ISO 527-2

 

Vydyne® R533H NT

聚酰胺66

Ascend Performance Materials Operations LLC

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 ISO 179/1eA

-30°C 10 12 kJ/m²

23°C 11 14 kJ/m²

简支梁无缺口冲击强度 ISO 179/1eU

-30°C 70 85 kJ/m²

23°C 80 90 kJ/m²

悬壁梁缺口冲击强度 ISO 180

-30°C 10 12 kJ/m²

23°C 12 14 kJ/m²

热性能 干燥 调节后的 单位制 测试方法

热变形温度

0.45 MPa, 未退火 260 -- °C ISO 75-2/B

1.8 MPa, 未退火 250 -- °C ISO 75-2/A

熔融温度 260 -- °C ISO 11357-3

线形热膨胀系数 ISO 11359-2

流动 : 23 到 55°C, 2.00 mm 2.1E-5 -- cm/cm/°C

横向 : 23 到 55°C, 2.00 mm 1.1E-4 -- cm/cm/°C

RTI Elec UL 746

0.750 mm 140 -- °C

1.50 mm 140 -- °C

3.00 mm 140 -- °C

RTI Imp UL 746

0.750 mm 125 -- °C

1.50 mm 125 -- °C

3.00 mm 125 -- °C

RTI UL 746

0.750 mm 140 -- °C

1.50 mm 140 -- °C

3.00 mm 140 -- °C

电气性能 干燥 调节后的 单位制 测试方法

体积电阻率 (0.750 mm) 1.0E+13 -- ohm•cm IEC 60093

介电强度 (1.00 mm) 20 -- kV/mm IEC 60243

耐电弧性 (3.00 mm) PLC 6 -- ASTM D495

漏电起痕指数 (3.00 mm) 250 到 399 -- V IEC 60112

高电弧燃烧指数(HAI) UL 746

0.750 mm PLC 0 --

1.50 mm PLC 0 --

3.00 mm PLC 0 --

高电压电弧起痕速率 (HVTR) PLC 1 -- UL 746

热丝引燃 (HWI) UL 746

0.750 mm PLC 4 --

1.50 mm PLC 3 --

3.00 mm PLC 4 --

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.750 mm HB --

1.50 mm HB --

3.00 mm HB --

灼热丝易燃指数 IEC 60695-2-12

0.750 mm 675 -- °C

1.50 mm 675 -- °C

3.00 mm 675 -- °C

 

Vydyne® R533H NT

聚酰胺66

Ascend Performance Materials Operations LLC

可燃性 干燥 调节后的 单位制   测试方法

热灯丝点火温度 IEC 60695-2-13

0.750 mm 700 -- °C

1.50 mm 700 -- °C

3.00 mm 700 -- °C

注射 干燥单位制

干燥温度 80.0°C

干燥时间 4.0hr

建议的最大回制料比例 25%

料筒后部温度 280 到 310°C

料筒中部温度 280 到 310°C

料筒前部温度 280 到 310°C

射嘴温度 280 到 310°C

加工（熔体）温度 285 到 305°C

模具温度 65.0 到 95.0°C

 

 

 

 

 

 

东莞市双帮塑胶原料有限公司大量销售塑料聚酰胺66  Ascend Performance Materials Operations LLC 尼龙66  美国首诺    尼龙66 Vydyne® R533H NT为塑料价格行情每天都有新的变化前天的报价不等于今天的报价。如果需要新的价格请电：13549213581，肖生。